The ternary compound Cadmium Manganese Telluride (“CMT”) is a magneto-optical material that is ICL’s newest crystal product.
This magneto-optical material has a giant Verdetconstant. Potential applications for this material (as well as CdMnHgTe which is under development ) include Faraday rotation devices (optical isolators in the range 630nm to 1100nm ), LEDs, spintronics, electromagnetic interference free devices, field tunable phase shifters, small coupled solar cells for fly-by-light applications, phased array radar with completely fiber-fed antennae, bomb detonators, optical isolation devices, advanced laser systems and harsh environment sensors.
At the optimal composition, absorption does not increase with pathlength (thickness) although transmission will vary. Absorption is composition dependent. The spectral data shown is for a 2mm thick sample. ICL’s standard processing for CdMnTe is flatness of 1 l, parallelism of 30 arc seconds, optical surface quality 60-40, reflection loss with broadband AR coating < 0.05% @ 880-1100nm, Max. Ø 19mm.
To learn more, visit our catalog for Magneto Crystals (CdMnTe).
Product Orientation Graphs
Optical Composition Information
Cd 0.55 Mn 0.45 Te
Transmission Range: 630nm to 22痠
Verdet constant: 0.67min/E*cm @ 904nm, 7min/E*cm @ 630nm
Absorbance: 0.3 cm-1 @ 800nm, ~0.2 cm-1 @ 904nm, 0.12 cm-1 @ 1000nm, <0.1cm-1@1100nm, 0.02 cm-1 – 0.03 cm-1 @1500nm
Extinction: Emin -28db, Emax -22db
Reflection Loss: 32%@904nm (2 surfaces)
Damage Threshold: 3j/cm2
Structure: cubic, Zink blende
Melting Point: ~ 1070° C
Solubility: Insoluble in water.